Aegis® NC73ZP
聚酰胺6
Honeywell
Technical Data
产品说明
The unique characteristics of Aegis NC73ZP is its ability to reduce the rate of oxygen transmission in film packaging and rigid packaging structures containing Nylon by 50% while maintaining or improving the flavor and aroma barrier, toughness and clarity. Aegis NC73ZP has been extruded and co-extruded as monolayer and multilayer film structures, it has also been injection molded providing a surface finish very similar to Nylon 6. The ease of processing allows vendors to utilize their present molding equipment and technology to broaden their market application of nylon.
总体
材料状态 • 已商用:停售
搜索 UL 黄卡 • Honeywell
供货地区 • 北美洲
性能特点 • 较低的气味转移性 • 可加工性,良好 • 清晰度,高
• 较低的味道转移性 • 良好的表面光洁度 • 韧性良好
用途 • 包装 • 硬包装
形式 • 颗粒料
加工方法 • 挤出 • 注射成型
物理性能 额定值 单位制 测试方法
比重 1.13g/cm³ ASTM D792
ISO 1183
熔流率 (260°C/1.0 kg) 4.6g/10 min ASTM D1238
机械性能 额定值 单位制 测试方法
拉伸模量 (23°C) 4000MPa ISO 527-2
拉伸应力 ISO 527-2
屈服, 23°C 92.0MPa
断裂, 23°C 89.0MPa
弯曲模量 (23°C) 3700MPa ISO 178
弯曲强度 (23°C) 126MPa ISO 178
薄膜 额定值 单位制 测试方法
透氧率 (23°C, 75% RH) cm³•mm/m²/atm/24 ASTM D3985
0.070 hr
热性能 额定值 单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 108°C ISO 75-2/A
熔融温度 220°C ISO 3146
补充信息
Izod Impact, ISO 180, -40°C: 3.7 J/m
Izod Impact, ISO 180, 23°C: 4.6 J/m
注射 额定值 单位制
干燥温度 80.0°C
建议的最大水分含量 0.080%
加工(熔体)温度 232 到 271°C
挤出 额定值 单位制
建议的最大水分含量 0.080%
第3气缸区温度 230 到 260°C
连接器温度 230 到 260°C
熔体温度 260 到 270°C
模具温度 260°C
|